DM | Sa J | Sa L | Si | |
Apparent density, kg·m−3 | 442.73 | 643.26 | 581.05 | 708.55 |
ε, % | 71.6 | 59.29 | 63.2 | 55.2 |
*Effective mean pore, μm | 2.3 | 6.8 | 4.9 | 4.7 |
*Dispersiveness of pore distribution, μm | 3.4 | 26 | 10 | 12 |
σT, mN/m | 2.6 | 7.5 | 6.1 | 5.7 |
γs, mN/m | 33.2 | 33.7 | 33.5 | 33.5 |
γd, mN/m | 30.1 | 30.1 | 30.1 | 30.1 |
γ+, mN/m | 0.28 | 0.28 | 0.28 | 0.28 |
γ−, mN/m | 8.6 | 11.6 | 10.7 | 10.5 |
γp, mN/m | 3.1 | 3.6 | 3.5 | 3.4 |
d | 0.91 | 0.89 | 0.90 | 0.90 |
p | 0.09 | 0.11 | 0.10 | 0.10 |
p+ | 0.01 | 0.01 | 0.01 | 0.01 |
p− | 0.26 | 0.34 | 0.32 | 0.31 |
Ye(97%), (g L/g S) | 0.29 | 0.22 | 0.26 | 0.24 |
Ye(75%), (g L/g S) | 0.11 | 0.08 | 0.09 | 0.08 |
Ye(49%), (g L/g S) | 0.06 | 0.05 | 0.05 | 0.05 |